Ceramic Bisque Firing Temperatures

This is the most common temperature range for industrial ceramics.

Ceramic bisque firing temperatures.

Generally bisque firing is done between cone 08 and cone 04 no matter what the maturation temperature of the clay and of the glazes that will be used later. It is bisque fired and then glaze fired. Bisque also refers to ceramic that has been fired but not yet glazed. Mostly yellow with a hint of orange.

What temperature should a bisque firing go to. The first firing of ceramic ware to make it strong enough to handle conveniently. For example a cone 10 clay bisque fired at cone 04 will be more porous than a cone 2 clay. Bisque firing refers to the first time newly shaped clay pots or greenware go through high temperature heating.

Firing clay from mud to ceramic. At the same time the clay body still is quite porous and absorbent. In low fire the bisque temperature is usually hotter than the firing temperature. For mid range material a kiln should be firing at a temperature between 2124 and 2264 1162 1240.

Raku clay is usually bisque fired to cone 04 to 1 clays that are to have crystalline glazes should be bisque fired slightly higher than normal i e. Very low fired overglazes and lusters are then applied to the already fired primary glaze. It is done to vitrify which means to turn it glasslike to a point that the pottery can have a glaze adhere to the surface. The ware will often not only go through a bisque firing but also a higher temperature glaze firing.

By cone 08 the ware is sintered and has become a ceramic material. Mid fire earthenware should be fired between cone 2 and cone 7. For example most commercial glazes recommend bisque firing to cone 04 and glaze firing to cone 06 which is cooler. The porous nature of bisque earthenware means that it readily absorbs water.

To start it must be bone dry. A body clay with underglaze can be bisque fired at cone 4 to 6 then have a low fire glaze firing at cone 06 to 04. The goal of bisque firing is to convert greenware to a durable semi vitrified porous stage where it can be safely handled during the glazing and decorating process. Gently heating a kiln and its contents above room temperature but below the boiling temperature of water.

The firing of the ware that results in the bisque article causes permanent chemical and physical. Bisque or biscuit firing. The temperature of bisque firing is usually at least 1000 c although higher temperatures are common. Low fire white terra cotta is generally bisque fired at cone 02 to 1.

The ware is returned to the kiln for a very low temperature firing in order to fuse the overglazes. The reason for this is to make sure all the carbon and other materials in the clay burn out during the bisque firing. Different clays do respond differently to the same bisque firing conditions.